HaHasmile® is a brand for selling dental materials, we are direct manufacturer for more than 10 years to sell zirconia blocks, PMMA blocks, Milling Burs, Grinding tools and other consumable materials experience, our dental materials have very high quality and our zirconia blocks monthly output 60000pcs. We can provide very stable and fast delivery.
3D Pro Multilayer Zirconia Bocks Product Description
Shape | 98mm/95mm/71mm |
Size | 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm/30mm |
| Color | A1/A2/A3/A3.5/A4/B1/B2/B3/B4/C1/C2/C3/C4/D2/D3/D4/OM1/OM2/OM3 |
Flexural strength
Layer | Percentage thickness | Strength | Translucency |
| 1st Layer | 20% | 800Mpa | 49% |
| 2nd Layer | 13% | 900Mpa | 47% |
| 3rd Layer | 13% | 950Mpa | 46% |
| 4th Layer | 13% | 1000Mpa | 45% |
| 5th Layer | 13% | 1050Mpa | 43% |
| 6th Layer | 30% | 1200Mpa | 42% |
Features:
6 Layers overlay, 11 Layers gradient;
Color, Strength, Transparency gradient;
From 42% to 49% gradient for transparency;
From 1200Mpa to 800Mpa gradient for strength;
Indications:
Inlay; Anterior Crown; Veneer; Full Crown Bridge; Posterior Crown; Full Arch Crown Bridge;
HaHasmile® 3D Pro Multilayer zirconia blocks are produced by CIP technology and pre-sintered in low temperature. Although the product has some strength, because of porosity, please handle carefully.
Chemical Composition
| Components | 3D Pro Multilayer Zirconia block |
| Nanometer zirconia powder | ≥98% |
| CeO₂ | ＜0.5% |
| Fe2O3 | ＜0.5% |
| Er2O3 | ＜0.5% |
| Other Oxides | ＜0.5% |
Mechanical Property
| Sintered Density g/cm³ | >6.02g/cm³ |
| Bending Strength Mpa | 800Mpa-1200Mpa |
| Translucency | 42%-49% |
| Hardness(Hv10) | 1250MPa |
| Sintered temperature(°C) | 1500°C |
| Radioactivity Bq.g-1 | <0.1 |
| Cytotoxicity | Level0 |
3D Pro Multilayer (1-3 units bridge) 8 hours
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 9.17℃/min | 1100℃ | 120min |
0℃/min | 1100℃ | 30min | |
3.33℃/min | 1500℃ | 120min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
13.33℃/min | 300℃ | 90min |
3D Pro Multilayer (4-6 units bridge) 10.5hours
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 7.33℃/min | 1100℃ | 150min |
0℃/min | 1100℃ | 30min | |
2.67℃/min | 1500℃ | 150min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
6.67℃/min | 300℃ | 180min |
3D Pro Multilayer (up to 7 units bridge) 13.5 hours
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 6.11℃/min | 1100℃ | 180min |
0℃/min | 1100℃ | 30min | |
2.22℃/min | 1500℃ | 180min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
4.0℃/min | 300℃ | 300min |
HaHasmile® is a brand for selling dental materials, we are direct manufacturer for more than 10 years to sell zirconia blocks, PMMA blocks, Milling Burs, Grinding tools and other consumable materials experience, our dental materials have very high quality and our zirconia blocks monthly output 60000pcs. We can provide very stable and fast delivery.
3D Pro Multilayer Zirconia Bocks Product Description
Shape | 98mm/95mm/71mm |
Size | 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm/30mm |
| Color | A1/A2/A3/A3.5/A4/B1/B2/B3/B4/C1/C2/C3/C4/D2/D3/D4/OM1/OM2/OM3 |
Flexural strength
Layer | Percentage thickness | Strength | Translucency |
| 1st Layer | 20% | 800Mpa | 49% |
| 2nd Layer | 13% | 900Mpa | 47% |
| 3rd Layer | 13% | 950Mpa | 46% |
| 4th Layer | 13% | 1000Mpa | 45% |
| 5th Layer | 13% | 1050Mpa | 43% |
| 6th Layer | 30% | 1200Mpa | 42% |
Features:
6 Layers overlay, 11 Layers gradient;
Color, Strength, Transparency gradient;
From 42% to 49% gradient for transparency;
From 1200Mpa to 800Mpa gradient for strength;
Indications:
Inlay; Anterior Crown; Veneer; Full Crown Bridge; Posterior Crown; Full Arch Crown Bridge;
HaHasmile® 3D Pro Multilayer zirconia blocks are produced by CIP technology and pre-sintered in low temperature. Although the product has some strength, because of porosity, please handle carefully.
Chemical Composition
| Components | 3D Pro Multilayer Zirconia block |
| Nanometer zirconia powder | ≥98% |
| CeO₂ | ＜0.5% |
| Fe2O3 | ＜0.5% |
| Er2O3 | ＜0.5% |
| Other Oxides | ＜0.5% |
Mechanical Property
| Sintered Density g/cm³ | >6.02g/cm³ |
| Bending Strength Mpa | 800Mpa-1200Mpa |
| Translucency | 42%-49% |
| Hardness(Hv10) | 1250MPa |
| Sintered temperature(°C) | 1500°C |
| Radioactivity Bq.g-1 | <0.1 |
| Cytotoxicity | Level0 |
3D Pro Multilayer (1-3 units bridge) 8 hours
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 9.17℃/min | 1100℃ | 120min |
0℃/min | 1100℃ | 30min | |
3.33℃/min | 1500℃ | 120min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
13.33℃/min | 300℃ | 90min |
3D Pro Multilayer (4-6 units bridge) 10.5hours
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 7.33℃/min | 1100℃ | 150min |
0℃/min | 1100℃ | 30min | |
2.67℃/min | 1500℃ | 150min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
6.67℃/min | 300℃ | 180min |
3D Pro Multilayer (up to 7 units bridge) 13.5 hours
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 6.11℃/min | 1100℃ | 180min |
0℃/min | 1100℃ | 30min | |
2.22℃/min | 1500℃ | 180min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
4.0℃/min | 300℃ | 300min |