HaHasmile® is a brand for selling dental materials, we are direct manufacturer for more than 10 years to sell zirconia blocks, PMMA blocks, Milling Burs, Grinding tools and other consumable materials experience, our dental materials have very high quality and our zirconia blocks monthly output 60000pcs. We can provide very stable and fast delivery.
UT Multilayer Zirconia Bocks Product Description
| Shape | 98mm/95mm/71mm |
| Size | 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm |
| Color | A1/A2/A3/A3.5/A4/B1/B2/B3/B4/C1/C2/C3/C4/D2/D3/D4/OM1/OM2/OM3 |
Features:
6 Layers Multilayer color;
Color, Strength, Transparency gradient;
From 49% gradient for transparency;
Strength shows up to 800Mpa;
Suitable for anterior teeth, crown and bridge;
UT Multilayer Zirconia blocks Indications:
Crown; Inlay; Onlay; Implant; Anterior;
HaHasmile® UT Multilayer zirconia blocks are produced by CIP technology and pre-sintered in low temperature. Although the product has some strength, because of porosity, please handle carefully.
Chemical Composition
| Components | UT Multilayer Zirconia block |
| Nanometer zirconia powder | ≥98% |
| CeO₂ | ＜0.5% |
| Fe2O3 | ＜0.5% |
| Er2O3 | ＜0.5% |
| Other Oxides | ＜0.5% |
Mechanical Property
| Sintered Density g/cm³ | >6.02g/cm³ |
| Bending Strength Mpa | 800Mpa |
| Translucency | 49% |
| Hardness(Hv10) | 1250MPa |
| Sintered temperature(°C) | 1450°C |
| Radioactivity Bq.g-1 | <0.1 |
| Cytotoxicity | Level0 |
UT Multilayer 1-5 units bridge
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 7.5℃/min | 1000℃ | 130min |
3.4℃/min | 1500℃ | 147min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
7℃/min | 800℃ | 100min | |
6.5℃/min | 20℃ | 120min |
UT Multilayer 6-10 units bridge
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 4℃/min | 1000℃ | 245min |
3℃/min | 1500℃ | 167min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
5℃/min | 800℃ | 140min | |
6.5℃/min | 20℃ | 120min |
HaHasmile® is a brand for selling dental materials, we are direct manufacturer for more than 10 years to sell zirconia blocks, PMMA blocks, Milling Burs, Grinding tools and other consumable materials experience, our dental materials have very high quality and our zirconia blocks monthly output 60000pcs. We can provide very stable and fast delivery.
UT Multilayer Zirconia Bocks Product Description
| Shape | 98mm/95mm/71mm |
| Size | 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm |
| Color | A1/A2/A3/A3.5/A4/B1/B2/B3/B4/C1/C2/C3/C4/D2/D3/D4/OM1/OM2/OM3 |
Features:
6 Layers Multilayer color;
Color, Strength, Transparency gradient;
From 49% gradient for transparency;
Strength shows up to 800Mpa;
Suitable for anterior teeth, crown and bridge;
UT Multilayer Zirconia blocks Indications:
Crown; Inlay; Onlay; Implant; Anterior;
HaHasmile® UT Multilayer zirconia blocks are produced by CIP technology and pre-sintered in low temperature. Although the product has some strength, because of porosity, please handle carefully.
Chemical Composition
| Components | UT Multilayer Zirconia block |
| Nanometer zirconia powder | ≥98% |
| CeO₂ | ＜0.5% |
| Fe2O3 | ＜0.5% |
| Er2O3 | ＜0.5% |
| Other Oxides | ＜0.5% |
Mechanical Property
| Sintered Density g/cm³ | >6.02g/cm³ |
| Bending Strength Mpa | 800Mpa |
| Translucency | 49% |
| Hardness(Hv10) | 1250MPa |
| Sintered temperature(°C) | 1450°C |
| Radioactivity Bq.g-1 | <0.1 |
| Cytotoxicity | Level0 |
UT Multilayer 1-5 units bridge
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 7.5℃/min | 1000℃ | 130min |
3.4℃/min | 1500℃ | 147min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
7℃/min | 800℃ | 100min | |
6.5℃/min | 20℃ | 120min |
UT Multilayer 6-10 units bridge
Start temp | Heating rate | Maximum temp | Holding time |
20℃ | 4℃/min | 1000℃ | 245min |
3℃/min | 1500℃ | 167min | |
0℃/min | 1500℃ | 120min | |
Cooling rate | Cooling to | Holding time | |
5℃/min | 800℃ | 140min | |
6.5℃/min | 20℃ | 120min |